E-ISSN 2548-0839
Volume : 7 Issue : 3 Year : 2025

Metrics

1.6
2023 IMPACT FACTOR
2.1
5 year Impact Factor
0.00061
Eigenfactor
3.4
2023 CiteScore
86/157
Journal Citation Reports (Clarivate, 2024)(Dentistry, Oral Surgery & Medicine (Science))
Quartile Q3
SCImago Journal & Country Rank
Cyclic Fatigue and Torsional Strength of a New Thermally Treated Reciprocating System [Eur Endod J]
Eur Endod J. 2022; 7(3): 198-202 | DOI: 10.14744/eej.2022.88700

Cyclic Fatigue and Torsional Strength of a New Thermally Treated Reciprocating System

Marco Antonio Zaiden Loureiro1, Pedro Henrique Souza Calefi2, Thalles Eduardo Ribeiro1, Rodrigo Ricci Vivan2, Marco Antonio Hungaro Duarte2, Patrícia Correia de Siqueira1, Daniel De Almeida Decurcio1
1Department of Oral Science, Federal University of Goiás, Faculty of Dentistry, Goiânia, Brazil
2Department of Dentistry, Endodontics and Dental Materials, University of São Paulo, Bauru Faculty of Dentistry, Bauru, Brazil

Objective: This study evaluated the resistance to cyclic fatigue and the torsional strength of Prima One Gold® and WaveOne Gold® reciprocating systems.
Methods: Cyclic fatigue was tested in an artificial canal with 60º curvature, a 5 mm radius of curvature at 22°C (n=10) and 36.5°C (n=10). The torsional strength test followed ISO 3630-1, measuring torque and deflection angle until fracture (n=10). The t-test was used to compare the two groups, and the significance level was set at 5%.
Results: The Prima One Gold group presented greater resistance to cyclic fatigue at room temperature (P=0.001) and body temperature (P<0.001). For the torsional resistance test, the Prima One Gold group had a lower maximum torque value (P=0.029), despite having a greater deflection angle (P<0.001).
Conclusion: The Prima One Gold group showed greater resistance to cyclic fatigue regardless of temperature and a greater deflection angle. The WaveOne Gold group showed a greater maximum torque value than the Prima One Gold group. (EEJ-2021-05-087)

Keywords: Alloys, mechanical tests, root canal preparation, shape memory alloys.